Hardox 400 500 Steel Plate

Hardox wear plate is the world's leading abrasion-resistant (AR) steel. Hardox is hard through and through, from the surface deep down to its core, giving you extended service life and high productivity in the most challenging environments.
Product introduction
Hardox 400 is an abrasion resistant steel with a nominal hardness of 400 HBW. Typical applications are components and structures subject to wear
Chemical Composition of Hardox 400 Wear Abrasion Resistant Sheet Plates
Technical data
Chemical Composition of Hardox 400 Wear Abrasion Resistant Sheet Plates
Plate C Si Mn P S Cr Ni Mo B CEV CET
thickness mm max % max % max % max % max % max % max % max % max % typv typv
3-(8) 0.15 0.7 1.6 0.025 0.01 0.3 0.25 0.25 0.004 0.33 0.23
08/20/13 0.15 0.7 1.6 0.025 0.01 0.5 0.25 0.25 0.004 0.37 0.27
(20)-32 0.18 0.7 1.6 0.025 0.01 1 0.25 0.25 0.004 0.48 0.29
(32)-45 0.22 0.7 1.6 0.025 0.01 1.4 0.5 0.6 0.004 0.57 0.31
(45)-51 0.22 0.7 1.6 0.025 0.01 1.4 0.5 0.6 0.004 0.57 0.38
(51)-80 0.27 0.7 1.6 0.025 0.01 1.4 1 0.6 0.004 0.65 0.41
(80)-130 0.32 0.7 1.6 0.025 0.01 1.4 1.5 0.6 0.004 0.73  

Mechanical Properties of Hardox 400 Wear Abrasion Resistant Sheet Plates
Grade Mechanical Property Charpy V Impact Test
HADOX 400 Yield Tensile Elongation Degree longitudinal
Min Mpa Mpa Min % -40 J
1000 1250 10 45

Hardox 450 is an abrasion-resistant steel with a nominal hardness of 450 HBW. Hardox 450 combines good bendability and weldability with an option for guaranteed impact toughness (Hardox 450 Tuf). The products can be used in many different components and structures that are subject to wear.
Chemical Properties Of hardox 450 Plate
HARDOX 450 Chemical Compositiom
Plate C Si Mn P S Cr Ni Mo B CEV CET
thickness mm max % max % max % max % max % max % max % max % max % typv typv
3-(8) 0.19 0.7 1.6 0.025 0.01 0.25 0.25 0.25 0.004 0.41 0.30
8-20 0.21 0.7 1.6 0.025 0.01 0.50 0.25 0.25 0.004 0.47 0.34
(20)-40 0.23 0.7 1.6 0.025 0.01 1.00 0.25 0.25 0.004 0.57 0.37
(40)-50 0.23 0.7 1.6 0.025 0.01 1.40 0.25 0.60 0.004 0.59 0.36
(50)-80 0.26 0.7 1.6 0.025 0.01 1.40 1.00 0.60 0.004 0.72 0.41

Plate thickness below 4 mm only after special agreement
CEV = C+Mn/6+(Cr+Mo+V)/5+(Cu+Ni)/15
CET = C + (Mn+Mo)/10+( Cr+ Cu)/20+ Ni/40

Mechanical Properties Of hardox 450 Plate
Mechanical properties of HARDOX 450
Grade Mechanical Property Charpy V Impact Test
HADOX 450 Yield Tensile Elongation Degree longitudinal
Min Mpa Mpa Min  % -40 J
1200 1400 10 40

Hardox 500 is a bendable and weldable abrasion-resistant steel at a nominal hardness of 500 HBW. Suitable for applications that demand higher wear resistance. Hardox 500 is a bendable and weldable abrasion-resistant steel, with a nominal hardness of 500 HBW. Suitable for applications that demand higher wear resistance.
HARDOX500 Chemical Composition
Plate C Si Mn P S Cr Ni Mo B CEV CET
thickness mm max % max % max % max % max % max % max % max % max % typv typv
04/13/13 0.27 0.7 1.6 0.025 0.01 1 0.25 0.25 0.004 0.49 0.34
(13)-32 0.29 0.7 1.6 0.025 0.01 1 0.5 0.3 0.004 0.62 0.41
(32)-40 0.29 0.7 1.6 0.025 0.01 1 1 0.6 0.004 0.64 0.43
(40)-80 0.3 0.7 1.6 0.025 0.01 1.5 1.5 0.6 0.004 0.74  

Mechanical Property HARDOX 500
Grade Mechanical Property Charpy V Impact Test
HADOX 500 HBW Thickness/Mpa Elongation Degree longitudinal
4-32MM 470-530 Min  % -40 J
(32)-80 450-540 10 40